| material property |
|
value |
imperial |
standard |
| tensile strength |
minimum* |
>1000MPa** |
145 ksi |
ASTM D3916 |
|
modulus (tensile)
|
typical*
minimum*
|
54.5 GPa
>50 GPa
|
7904ksi
7250ksi
|
ASTM D3916
|
|
shear strength (single sided)
|
typical
minimum
|
260 MPa
230 MPa
|
37.7 ksi
33.4 ksi
|
ASTM B769-94
|
|
shear strength (double sided)
|
typical
minimum
|
520 MPa
460 MPa
|
75.4 ksi
66.7 ksi
|
ASTM B769-94
|
|
compressive strength (longitudinal)
|
typical
Minimum
|
690 MPa
500 MPa
|
100 ksi
72.5 ksi
|
ASTM D695
|
|
moisture absorption
|
typical
|
0.024%
|
|
BS2782 pt 4,
method 430/
ISO 62-1980
|
| Thermal conductivity |
typical |
0.25 W/mK−¹ |
|
ASTM C117 |
| electrical strength |
typical |
5 - 40 kV/mm |
|
DIN 53 481 |
| Volume resistivity |
typical |
10¹ºΩ.m |
|
DIN 53 482 |
| dielectric constant |
typical |
< 5 |
|
DIN 53 483 |
|
magnetic properties
density
|
typical
|
non-magnetic
1.9 - 2.1 g/cm³
|
|
|
*tensile strength and modululus are typically higher for smaller dialeter bars.
**based on 20mm diameter.
|